From: Analytical effect of stabilizer volume and shape on zircon U–Pb dating by nanosecond LA-ICP-QMS
Stabilizer type/volume (mL) | Sample no. | 206Pb/238U ratio | 1σ | Stabilizer type/volume (mL) | Sample no. | 206Pb/238U ratio | 1σ |
---|---|---|---|---|---|---|---|
Cylinder/21.2 | PL-1-1 | 0.05371 | 0.00091 | Squid/16.3 | PL-7-1 | 0.05453 | 0.00079 |
PL-1-2 | 0.05372 | 0.00092 | PL-7-2 | 0.05325 | 0.00075 | ||
PL-1-3 | 0.05357 | 0.00087 | PL-7-3 | 0.05406 | 0.00080 | ||
PL-1-4 | 0.05353 | 0.00081 | PL-7-4 | 0.05345 | 0.00068 | ||
PL-1-5 | 0.05261 | 0.00085 | PL-7-5 | 0.05393 | 0.00067 | ||
Average | 0.05343 | 0.00087 | Average | 0.05384 | 0.00074 | ||
Cylinder/25.1 | PL-2-1 | 0.05512 | 0.00102 | Cubic/18.0 | PL-8-1 | 0.05491 | 0.00094 |
PL-2-2 | 0.05672 | 0.00113 | PL-8-2 | 0.05450 | 0.00086 | ||
PL-2-3 | 0.05800 | 0.00094 | PL-8-3 | 0.05491 | 0.00081 | ||
PL-2-4 | 0.05893 | 0.00097 | PL-8-4 | 0.05458 | 0.00081 | ||
PL-2-5 | 0.05982 | 0.00099 | PL-8-5 | 0.05414 | 0.00082 | ||
Average | 0.05772 | 0.00101 | Average | 0.05461 | 0.00085 | ||
Cylinder/35.3 | PL-3-1 | 0.05453 | 0.00077 | Ball/14.1 | PL-9-1 | 0.05315 | 0.00078 |
PL-3-2 | 0.05392 | 0.00090 | PL-9-2 | 0.05361 | 0.00079 | ||
PL-3-3 | 0.05438 | 0.00080 | PL-9-3 | 0.05420 | 0.00073 | ||
PL-3-4 | 0.05412 | 0.00080 | PL-9-4 | 0.05488 | 0.00063 | ||
PL-3-5 | 0.05393 | 0.00074 | PL-9-5 | 0.05523 | 0.00073 | ||
Average | 0.05417 | 0.00080 | Average | 0.05421 | 0.00073 | ||
Cylinder/125 | PL-4-1 | 0.05257 | 0.00072 | Without stabilizer/– | PL-10-1 | 0.05540 | 0.00101 |
PL-4-2 | 0.05250 | 0.00072 | PL-10-2 | 0.05435 | 0.00100 | ||
PL-4-3 | 0.05356 | 0.00065 | PL-10-3 | 0.05614 | 0.00122 | ||
PL-4-4 | 0.05385 | 0.00072 | PL-10-4 | 0.05602 | 0.00111 | ||
PL-4-5 | 0.05775 | 0.00084 | PL-10-5 | 0.05549 | 0.00102 | ||
PL-4-6 | 0.05592 | 0.00087 | Average | 0.05548 | 0.00107 | ||
Average | 0.05472 | 0.00076 | PL-11-1 | 0.05297 | 0.00095 | ||
Cylinder/21.2 (with 1.0 g stainless wire) | PL-5-1 | 0.05222 | 0.00068 | PL-11-2 | 0.05303 | 0.00096 | |
PL-5-2 | 0.05326 | 0.00074 | PL-11-3 | 0.05305 | 0.00094 | ||
PL-5-3 | 0.05324 | 0.00067 | PL-11-4 | 0.05203 | 0.00087 | ||
PL-5-4 | 0.05369 | 0.00063 | PL-11-5 | 0.05326 | 0.00079 | ||
PL-5-5 | 0.05380 | 0.00078 | Average | 0.05287 | 0.00090 | ||
Average | 0.05324 | 0.00070 |